日本东丽 PA66 CM3211G-35 UB1
材料属性：35%玻纤 增强
应用方面：汽车应用
特性：耐氯化钙 增强
加工方式：注射成型


Physical Nominal Value Unit Test Method
Density (23°C) 1.36 g/cm³ ISO 1183
Molding Shrinkage 1 Internal Method
Across Flow : 3.00 mm 0.50 to 0.80 %
Flow : 3.00 mm 0.20 to 0.40 %
Water Absorption 2 ISO 62
24 hr, 23°C 0.40 %
Saturation, 23°C 3.0 %
Mechanical Nominal Value Unit Test Method
Tensile Strength ISO 527-2
-40°C 280 MPa
23°C 195 MPa
80°C 120 MPa
Tensile Strain ISO 527-2
Break, -40°C 3.0 %
Break, 23°C 3.0 %
Break, 80°C 5.0 %
Flexural Modulus ISO 178
-40°C 11000 MPa
23°C 9500 MPa
80°C 4800 MPa
Flexural Stress ISO 178
-40°C 370 MPa
23°C 290 MPa
80°C 160 MPa
Impact Nominal Value Unit Test Method
Charpy Notched Impact Strength ISO 179
-40°C 10.0 kJ/m²
23°C 13.5 kJ/m²
Charpy Unnotched Impact Strength ISO 179
-40°C 89.0 kJ/m²
23°C 94.5 kJ/m²
Hardness Nominal Value Unit Test Method
Rockwell Hardness ISO 2039-2
M-Scale, 23°C 93
R-Scale, 23°C 120
Thermal
Deflection Temperature Under Load Nominal Value Unit Test Method
0.45 MPa, Unannealed 228 °C ISO 75-2/B
1.8 MPa, Unannealed 225 °C ISO 75-2/A
Melting Temperature 265 °C DSC
Thermal Conductivity 0.42 W/m/K
Coefficient of Linear Thermal Expansion 2 to 3 cm^-5/cm/°C ISO 11359-2
Electrical Nominal Value Unit Test Method
Volume Resistivity 1.0E+13 ohms·m IEC 60093
Flammability
Flame Rating 3 (1.6 mm, Equivalent) Nominal Value
HB Unit Test Method
Internal Method