日本东丽 PA66 CM3003 G 1000
材料属性：耐磨级
应用方面：外壳；OA设备；电器用具
特性：非增强
加工方式：注射成型


Physical Nominal Value Unit Test Method
Density (23°C) 1.19 g/cm³ ISO 1183
Molding Shrinkage 1
Across Flow : 3.00 mm
1.20 to 2.00
% Internal Method
Flow : 3.00 mm 0.50 to 1.20 %
Water Absorption 2
24 hr, 23°C
1.1
% ISO 62
Saturation, 23°C 7.5 %
Mechanical Nominal Value Unit Test Method
Tensile Strength (23°C) 100 MPa ISO 527-2
Tensile Strain (Break, 23°C) 2.5 % ISO 527-2
Flexural Modulus (23°C) 3200 MPa ISO 178
Flexural Stress (23°C) 140 MPa ISO 178
Taber Abrasion Resistance (1000 Cycles) 7 mg ISO 9352
Coefficient of Friction - vs. Metal 3 0.10 to 0.15 Suzuki Method
Impact Nominal Value Unit Test Method
Charpy Notched Impact Strength (23°C) 4.0 kJ/m² ISO 179
Hardness
Rockwell Hardness (R-Scale, 23°C) Nominal Value
119 Unit Test Method
ISO 2039-2
Thermal
Deflection Temperature Under Load
0.45 MPa, Unannealed Nominal Value
220 Unit  °C Test Method  ISO 75-2/B
Melting Temperature 265 °C DSC
Coefficient of Linear Thermal Expansion 7 to 8 cm^-5/cm/°C ISO 11359-2
Flammability
Flame Rating (1.5 mm, NC) Nominal Value
V-2 Unit Test Method   UL 94