日本东丽 PA66 CM3003G-30
材料属性：30%玻纤增强；耐磨级
应用方面：外壳；OA设备；电器用具
特性：
加工方式：注射成型


Physical Nominal Value Unit Test Method
Density (23°C) 1.38 g/cm³ ISO 1183
Molding Shrinkage 1
Across Flow : 3.00 mm
0.60 to 0.80
% Internal Method
Flow : 3.00 mm 0.20 to 0.50 %
Water Absorption 2
24 hr, 23°C
0.60
% ISO 62
Saturation, 23°C 5.5 %
Mechanical Nominal Value Unit Test Method
Tensile Strength (23°C) 170 MPa ISO 527-2
Tensile Strain (Break, 23°C) 3.0 % ISO 527-2
Flexural Modulus (23°C) 10000 MPa ISO 178
Flexural Stress (23°C) 270 MPa ISO 178
Taber Abrasion Resistance (1000 Cycles) 23 mg ISO 9352
Coefficient of Friction - vs. Metal 3 0.20 Suzuki Method
Impact Nominal Value Unit Test Method
Charpy Notched Impact Strength (23°C) 10.0 kJ/m² ISO 179
Hardness
Rockwell Hardness (R-Scale, 23°C) Nominal Value
121 Unit Test Method
ISO 2039-2
Thermal Nominal Value Unit Test Method
Deflection Temperature Under Load
0.45 MPa, Unannealed
262
°C
ISO 75-2/B
1.8 MPa, Unannealed 255 °C ISO 75-2/A
Melting Temperature 265 °C DSC
Coefficient of Linear Thermal Expansion 2 to 3 cm^-5/cm/°C ISO 11359-2
Flammability
Flame Rating (1.5 mm, NC) Nominal Value
HB Unit Test Method
UL 94