U121/PA6 U121 日本东丽

本公司秉持“事物的存在意义在于延续”理念。
万物秉持可持续性才能长久存在下去——best售后

日本东丽 PA6 U121
材料属性：冲击改性
应用方面：连接器
特性：高冲击
加工方式：注射成型


Physical Dry Water Absorption Unit Test Method
Density (23°C) 1.09 -- g/cm³ ISO 1183
Molding Shrinkage 1
(3.00 mm) 1.20 to 1.30 -- % Internal Method
Water Absorption 2 ISO 62
24 hr, 23°C 1.7 -- %
Saturation, 23°C 8.0 -- %
Mechanical Dry Water Absorption Unit Test Method
Tensile Strength ISO 527-2
-40°C 90 70 MPa
23°C 60 35 MPa
Tensile Strain ISO 527-2
Break, -40°C 13 19 %
Break, 23°C > 50 > 50 %
Flexural Modulus ISO 178
-40°C 2500 2500 MPa
23°C 2000 800 MPa
Flexural Stress ISO 178
-40°C 115 100 MPa
23°C 80 35 MPa
Taber Abrasion ISO 9352
Resistance
1000 Cycles 6 to 7 -- mg
Impact Dry Water Absorption Unit Test Method
Charpy Notched Impact ISO 179
Strength
-40°C 10.5 15.5 kJ/m²
23°C 16.5 65.6 kJ/m²
Charpy Unnotched Impact ISO 179
Strength
23°C No Break No Break
Hardness Dry Water Absorption Unit Test Method
Rockwell Hardness ISO 2039-2
R-Scale, 23°C 114 --
Thermal Dry Water Absorption Unit Test Method
Deflection Temperature Under Load
0.45 MPa, Unannealed 160 -- °C ISO 75-2/B
1.8 MPa, Unannealed 57 -- °C ISO 75-2/A
Melting Temperature 225 -- °C DSC
Coefficient of Linear 9 to 10 -- cm^-5/cm/°C ISO 11359-2
Flammability
Flame Rating (1.5 mm)
Additional Information
Dry Dry
HB


Water absorption Moisture Content 2.8% Water Absorption
-- Unit Test Method
UL 94